性 能
Properties
|
测试方法
Test Method |
条 件
Terms |
单 位
Units |
Unreinforced UL-HBtype |
5010L |
Medium Viscosity |
Percentage of filler and
reinforcing material |
-- |
-- |
-- |
-- |
-- |
-- |
% |
0 |
物理性能 Physical properties
|
比 重 Density |
ISO 1183 |
-- |
g/cm3 |
1.31 |
吸水率 Water absorption |
-- |
23degC,Underwater |
% |
0.10 |
流变性能 Rheological properties |
熔体质量流动速率
Melt Mass-flow Rate |
ISO 1133 |
Temperature Load |
g/10min
cm3/10min
degC
kg |
25
23
250
2.16 |
熔体体积流动速率
Melt Volume-flow Rate |
成型收缩率
Moulding shrinkage(1mmt) |
-- |
MD
TD |
% |
1.5
1.4 |
成型收缩率
Moulding shrinkage(3mmt) |
-- |
MD
TD |
% |
2.2
2.0 |
机械性能 Mechanical properties |
拉伸模量 Tensile modulus |
ISO 527-1
, 527-2 |
--- |
Mpa |
2400 |
屈服应力 Yield stress |
54 |
屈服应变 Yield strain |
% |
4.4 |
标称断裂伸长率
Nominal strain at break |
120 |
伸长率 50% 应力
Stress at 50% strain |
Mpa |
-- |
断裂应力 Stress at break |
-- |
断裂伸长率 Srtain at break |
% |
-- |
挠曲强度 Flexural strength |
ISO 178 |
--- |
Mpa |
85
2400 |
挠曲模量 Flexural modulus |
摆式冲击强度
Charpy impact strength |
ISO 179-1
, 179-2 |
23 degC |
kJ/㎡ |
NB |
摆式冲击强度（有缺口）
Charpy notched impact strength |
23 degC |
kJ/㎡ |
5 |
热性能 Thermal properties |
熔点 Melting temperature |
ISO 11357-3 |
|
degC |
224 |
负荷挠曲温度
Temperature of deflection under load |
ISO 75-1
, 75-2 |
1.80Mpa
0.45Mpa |
DegC |
54
136 |
线性热膨胀系数
Coefficient of Linear thermal expansion |
ISO 11359-2 |
MD
TD |
1/degC |
11E-05
11E-05 |
燃烧性 Flammability |
UL94 |
0.8mmt |
-- |
HB |
电性能 Electrical properties |
|
介电常数 Relative permittivity |
IEC 60250 |
1MHz |
-- |
3.2 |
介电损耗因数 Dissipation factor |
IEC 60250 |
1MHz |
-- |
0.020 |
体积电阻系数 Volume resistivity |
IEC 60093 |
-- |
ohm-m |
1.E+14 |
表面电阻系数 Surface resistivity |
IEC 60093 |
-- |
ohm |
1.E+15 |
导 电 强 度 Electric strength |
IEC 60243-1 |
1mmt
2mmt |
MV/m |
22
17 |
比较跟踪索引
Comparative tracking index |
UL 746A |
-- |
-- |
PLC 0 |